Process for making silver nanostructures and copolymer useful in such process

ABSTRACT

A process for making silver nanostructures, which includes the step of reacting at least one polyol and at least one silver compound that is capable of producing silver metal when reduced, in the presence of: (a) a source of chloride or bromide ions, and (b) at least one copolymer that comprises: (i) one or more first constitutional repeating units that each independently comprise at least one pendant saturated or unsaturated, five-, six-, or seven-membered, acylamino- or diacylamino-containing heterocylic ring moiety per constitutional repeating unit, and (ii) one or more second constitutional repeating units, each of which independently differs from the one or more first nonionic constitutional repeating units, and has a molecular weight of greater than or equal to about  500  grams per mole, is described herein.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a divisional application of U.S. application Ser. No. 14/040,406, filed Sep. 27, 2013, hereby incorporated by reference, which claims the benefit of U.S. provisional application No. 61/706,280 filed Sep. 27, 2012, the entirety of which is hereby incorporated by reference.

FIELD OF THE INVENTION

The present invention relates to a process for making silver nanostructures and a copolymer useful in such process.

BACKGROUND

Transparent conductors, such as Indium Tin Oxide (ITO), combine the electrical conductivity of metal with the optical transparency of glass and are useful as components in electronic devices, such as in display devices. Flexibility is likely to become a broader challenge for ITO, which does not seem well suited to the next generation of display, lighting, or photovoltaic devices. These concerns have motivated a search for replacements using conventional materials and nanomaterials. There is variety of technical approaches for developing ITO substitutes and there are four areas in which the alternative compete: price, electrical conductivity, optical transparency, and physical resiliency.

Electrically conductive polymers, such as polythiophene polymers, particularly a polymer blend of poly(3,4-ethylenedioxythiophene) and poly(styrene sulfonate) (“PEDOT-PSS”) have been investigated as possible alternatives to ITO. The electrical conductivity of electrically conductive polymers is typically lower than that of ITO, but can be enhanced through the use of conductive fillers and dopants.

Processes for making electrically conductive metal nanostructures are known. Ducamp-Sanguesa, et. al., Synthesis and Characterization of Fine and Monodisperse Silver Particles of Uniform Shape, Journal of Solid State Chemistry 100, 272-280 (1992) and U.S. Pat. No. 7,585,349, issued Sep. 8, 2009, to Younan Xia, et. al., each describe synthesis of silver nanowires by reduction of a silver compound in a glycol in the presence of polyvinylpyrrolidone.

Structures comprising a network of silver nanowires encapsulated in an electrically conductive polymer have been described. U.S. Patent Application Publication No. 2008/0259262 describes forming such structures by depositing a network of metal nanowires on a substrate and then forming a conductive polymeric film in situ, e.g., by electrochemical polymerization using the metal nanowire network as an electrode. U.S. Patent Application Publication No. 2009/0129004 describes forming such structures by filtration of a silver nanowire dispersion to form a silver nanowire network, heat treating the network, transfer printing the heat treated network, and encapsulating the transfer printed network with polymer.

The performance of such electrically conductive polymer/silver nanowire composite films is, in some cases, comparable to that of ITO but the processing required to obtain composite films that exhibit that level of performance is quite demanding, for example, the above described films require processing steps, such as thermal treatment and compression, in order to ensure that sufficient electrical connections are made among the electrically conductive nanowires of the composite film to provide a film having high conductivity and transparency. There is an ongoing unresolved interest in increasing the electrical conductivity and optical transparency of electrically conductive polymer films.

SUMMARY OF THE INVENTION

In a first aspect, the present invention is directed to a process for making silver nanostructures, comprising reacting at least one polyol and at least one silver compound that is capable of producing silver metal when reduced, in the presence of:

-   (a) a source of chloride or bromide ions, and -   (b) at least one copolymer that comprises:     -   (i) one or more first constitutional repeating units that each         independently comprise at least one pendant saturated or         unsaturated, five-, six-, or seven-membered, acylamino- or         diacylamino-containing heterocylic ring moiety per         constitutional repeating unit, and     -   (ii) one or more second constitutional repeating units, each of         which independently differs from the one or more first nonionic         constitutional repeating units,     -   and has a molecular weight of greater than or equal to about 500         grams per mole.

In a second aspect, the present invention is directed to a copolymer, comprising, based on 1000 constitutional repeating units of the copolymer:

-   -   from 800 to 999 first constitutional repeating units, each         independently comprising at least one pendant saturated or         unsaturated, five-, six-, or seven-membered, acylamino- or         diacylamino-containing heterocylic ring moiety per         constitutional repeating unit, and     -   from 1 to 200 second constitutional repeating units, each         independently comprising at least one pendant organic moiety         that: (i) is selected from ionic organic moieties and nonionic         organic moieties, and (ii) is not a saturated or unsaturated,         five-, six-, or seven-membered, acylamino- or         diacylamino-containing heterocylic ring moiety,

-   and having a molecular weight of greater than or equal to about 500     grams per mole.

In a third aspect, the present invention is directed to a process for making silver nanostructures, comprising reacting at least one polyol and at least one silver compound that is capable of producing silver metal when reduced, in the presence of:

-   (a) a source of chloride or bromide ions, and -   (b) at least one copolymer that comprises:     -   (i) one or more first constitutional repeating units that each         independently comprise at least one pendant saturated or         unsaturated, five-, six-, or seven-membered, acylamino- or         diacylamino-containing heterocylic ring moiety per         constitutional repeating unit, and     -   (ii) one or more second constitutional repeating units, each of         which independently differs from the one or more first nonionic         constitutional repeating units,     -   and has a molecular weight of greater than or equal to about 500         grams per mole; and -   (c) at least one base.

BRIEF DESCRIPTION OF THE DRAWINGS

FIGS. 1(a) and 1(b) show representative 1H NMR and FTIR spectra of the poly(vinylpyrrolidone-co-diallyldimethylammonium nitrate) random copolymers (“poly(VP-co-DADMAN)” copolymers) of Examples 1A-1E.

FIG. 2 shows characteristics of the silver nanostructures of Examples 2A-2G and Comparative Examples C1-C3, as a function of the amount of silver nitrate added and the composition of the polymeric protectant, wherein each cross corresponds to one of the Examples.

FIG. 3 shows length distributions of the nanowire products obtained using poly(VP-co-DADMAN) copolymer with 16 percent by weight (“wt %”) DADMAN content at different concentrations of silver nitrate.

FIG. 4 shows arithmetic average length distribution of nanowire products obtained using poly(VP-co-DADMAN) copolymer with 1 wt % DADMAN content at different concentrations of the copolymer at two different amounts of silver nitrate.

FIG. 5 shows the titration curve of the “Lot A” ethylene glycol used in Examples 2, 3, 4, and comparative examples C2A-C2C.

FIG. 6 shows a TEM image of the silver nanowires of Example 2A.

FIG. 7 shows the titration curve of the “Lot B” ethylene glycol used in Examples 7, 8, and 9.

FIG. 8 shows an SEM image of the silver nanowires of Example 7 produced with the addition of lithium hydroxide.

FIG. 9 shows an image of the silver nanowires of Example 7 produced with the addition of lithium hydroxide as seen with an optical microscope.

FIG. 10 shows an image of the silver nanowires of Example 8 produced with the addition of potassium hydroxide as seen with an optical microscope.

FIG. 11 shows an image of the silver nanowires of Example 9 produced with the addition of sodium hydroxide as seen with an optical microscope.

DETAILED DESCRIPTION OF THE INVENTION

As used herein, the following terms have the following meanings:

-   -   “doped” as used herein in reference to an electrically         conductive polymer means that the electrically conductive         polymer has been combined with a polymeric counterion for the         electrically conductive polymer, which polymeric counterion is         referred to herein as “dopant”, and is typically a polymeric         acid, which is referred to herein as a “polymeric acid dopant”,     -   “doped electrically conductive polymer” means a polymer blend         comprising an electrically conductive polymer and a polymeric         counterion for the electrically conductive polymer,     -   “electrically conductive polymer” means any polymer or polymer         blend that is inherently or intrinsically, without the addition         of electrically conductive fillers such as carbon black or         conductive metal particles, capable of electrical conductivity,         more typically to any polymer or oligomer that exhibits a bulk         specific conductance of greater than or equal to 10⁻⁷ Siemens         per centimeter (“S/cm”), unless otherwise indicated, a reference         herein to an “electrically conductive polymer” include any         optional polymeric acid dopant,     -   “electrically conductive” includes conductive and         semi-conductive,     -   “electronic device” means a device that comprises one or more         layers comprising one or more semiconductor materials and makes         use of the controlled motion of electrons through the one or         more layers,     -   “layer” as used herein in reference to an electronic device,         means a coating covering a desired area of the device, wherein         the area is not limited by size, that is, the area covered by         the layer can, for example, be as large as an entire device, be         as large as a specific functional area of the device, such as         the actual visual display, or be as small as a single sub-pixel.

As used herein, the following terms have the following meanings:

-   -   “alkyl” means a monovalent straight, branched or cyclic         saturated hydrocarbon radical, more typically, a monovalent         straight or branched saturated (C₁-C₄₀)hydrocarbon radical, such         as, for example, methyl, ethyl, n-propyl, isopropyl, n-butyl,         isobutyl, tert-butyl, hexyl, octyl, hexadecyl, octadecyl,         eicosyl, behenyl, tricontyl, and tetracontyl,     -   “cycloalkyl” means a saturated hydrocarbon radical, more         typically a saturated (C₅-C₂₂) hydrocarbon radical, that         includes one or more cyclic alkyl rings, which may optionally be         substituted on one or more carbon atoms of the ring with one or         two (C₁-C₆)alkyl groups per carbon atom, such as, for example,         cyclopentyl, cycloheptyl, cyclooctyl,     -   “heteroalkyl” means an alkyl group wherein one or more of the         carbon atoms within the alkyl group has been replaced by a         hetero atom, such as nitrogen, oxygen, or sulfur,     -   “heterocyclic” means an cyclic hydrocarbon group in which one or         more of the ring carbon atoms has been replaced by a hetero         atom, such as nitrogen, oxygen, or sulfur,     -   “alkylene” refers to a divalent alkyl group including, for         example, methylene, and poly(methylene),     -   “alkenyl” means an unsaturated straight or branched hydrocarbon         radical, more typically an unsaturated straight, branched,         (C₂-C₂₂) hydrocarbon radical, that contains one or more         carbon-carbon double bonds, including, for example, ethenyl,         n-propenyl, and iso-propenyl,     -   “aryl” means an unsaturated hydrocarbon radical that contains         one or more six-membered carbon rings in which the unsaturation         may be represented by three conjugated carbon-carbon double         bonds, wherein one or more of the ring carbons may be         substituted with one or more hydroxy, alkyl, alkenyl, alkoxy,         halo, or alkylhalo substituents, such as, for example, phenyl,         methylphenyl, trimethylphenyl, nonylphenyl, chlorophenyl,         trichloromethylphenyl, naphthyl, and anthryl, and     -   “aralkyl” means an alkyl group substituted with one or more aryl         groups, more typically a (C₁-C₁₈)alkyl substituted with one or         more (C₆-C₁₄)aryl substituents, such as, for example,         phenylmethyl, phenylethyl, and triphenylmethyl, and     -   “(C_(x)-C_(y))” in reference to an organic group, wherein x and         y are each integers, means that the group may contain from x         carbon atoms to y carbon atoms per group.

Addition of the prefix “(meth)” to a group name, such as “acrylate”, “acrylic”, “acrylamide”, “acrylamido”, or “allyl” to form terms such as “(meth)acrylate, “(meth)acrylic”, “(meth)acrylamide, “(meth)acrylamido”, and “(meth)allyl” is used herein to indicate the methyl-subsitituted and/or the non-methyl-subsitituted homologs of such groups. For example, the term “ethyl (meth)acrylate”, as used herein means ethyl acrylate, ethyl methacrylate, or a mixture thereof.

As used herein in reference to an organic or inorganic moiety, the following terms have the following meanings:

-   -   “cationic” means that the moiety carries a net positive         electrical charge,     -   “anionic” means that the moiety carries a net negative         electrical charge,     -   “amphoteric” and “zwitterionic” mean that the moiety has no net         electrical charge, but carries, or under certain pH conditions,         may carry both a localized negative electrical charge and a         localized positive electrical charge, and     -   “nonionic” means that the moiety is carries no net electrical         charge no localized negative electrical charge and no localized         positive electrical charge.

As used herein in reference to a polymer or copolymer molecule, the following terms have the following meanings:

-   -   “constitutional repeating unit” means the smallest         constitutional unit, the repetition of which constitutes a chain         or a block of the polymer or copolymer molecule,     -   “constitutional unit” means an atom or group of atoms, including         pendant atoms or groups, if any, comprising a part of the         essential structure of the polymer or copolymer molecule or of a         block or chain of the polymer or copolymer molecule,     -   “chain” means the whole or a portion of the polymer or copolymer         molecule, comprising a linear or branched sequence of one or         more constitutional units between two boundary constitutional         units, each of which may be either an end-group, a branch point         or an otherwise-designated characteristic feature of the polymer         or copolymer molecule, and     -   “block” means, in reference to a copolymer, a portion of the         copolymer, comprising two or more constitutional units that has         at least one feature which is not present in the adjacent         portions of the copolymer.

The dimensions referred to herein in regard to bulk nanostructure materials are averaged dimensions obtained by sampling individual nanostructures contained in the bulk material wherein the lengths are obtained using optical microscopy, and the diameters are determined using electron microscopy. Using this process, a sample of about 150 nanostructures are measured to determine the lengths, and a sample of about 10 nanostructures are measured to determine the diameters. An average diameter, average length, and average aspect ratio are then determined for the nanostructures examined as follows. Unless otherwise indicated, nanostructure dimensions are given as arithmetic averages of the measured nanowire population. In the case of anisotropic nanostructures, such as nanowires, lengths may also be given as length weighted average lengths, as determined by first taking the length of each nanowire and dividing it by the sum of the lengths of all nanowires measured to derive a quantity W₁, which is the percent contribution of the single nanowire to the sum length of all nanowires, then, for each of the measured nanowires, deriving a weighted length by multiplying the length of the nanowire by its respective W₁ value, and finally taking the arithmetic average of the weighted lengths of the measured nanowires to derive the length weighted average length of the nanowire population. Aspect ratios of anisotropic nanostructures are determined by dividing the length weighted average length of the nanowire population by the average diameter of the anisotropic nanostructure population.

As used herein, the term “nanostructures” generally refers to nano-sized structures, at least one dimension of which is less than or equal to 2000 nm, more typically less than or equal to 500 nm, even more typically, less than or equal to 250 nm, or less than or equal to 100 nm, or less than or equal to 50 nm, or less than or equal to 25 nm. The anisotropic electrically conductive nanostructures can be of any anisotropic shape or geometry. As used herein, the terminology “aspect ratio” in reference to a structure means the ratio of the structure's longest characteristic dimension to the structure's next longest characteristic dimension. In one embodiment, the anisotropic electrically conductive nanostructures have an elongated shape with a longest characteristic dimension, i.e., a length, and a next longest characteristic dimension, i.e., a width or diameter, with an aspect ratio of greater than 1.

The at least one polyol serves as liquid medium in which to conduct the reaction and as a reducing agent that reduces the silver compound to silver metal. Suitable polyols are organic compounds having a core moiety comprising at least 2 carbon atoms, which may optionally further comprise one or more heteroatoms selected from N and O, wherein the core moiety is substituted with at least 2 hydroxyl groups per molecule and each hydroxyl group is attached to a different carbon atom of the core moiety. Suitable polyols are known and include, for example, alkylene glycols, such as ethylene glycol, propylene glycols, and butanediols, alkylene oxide oligomers, such as diethylene glycol, triethylene glycol, tetraethylene glycol, dipropylene glycol, and polyalkylene glycols, such as polyethylene glycol and polypropylene glycol, provided that such polyalkylene glycol is liquid at the reaction temperature, triols, such as, for example, glycerol, trimethylolpropane, triethanolamine, and trihydroxymethylaminomethane, and compounds having more than 3 hydroxyl groups per molecule, as well as mixtures of two or more of any of such compounds. In one embodiment, the polyol comprises ethylene glycol.

Suitable silver compounds that are capable of producing silver metal when reduced are known and include silver oxide, silver hydroxide, organic silver salts, and inorganic silver salts, such as silver nitrate, silver nitrite, silver sulfate, silver halides such as silver chloride, silver carbonates, silver phosphate, silver tetrafluoroborate, silver sulfonate, silver carboxylates, such as, for example, silver formate, silver acetate, silver propionate, silver butanoate, silver trifluoroacetate, silver acetacetonate, silver lactate, silver citrate, silver glycolate, silver tosylate, silver tris(dimethylpyrazole)borate, as well as mixtures of two or more of such compounds. In one embodiment, the silver compound capable of producing silver metal when reduced comprises silver nitrate (AgNO₃).

Suitable sources of chloride and/or bromide ions include hydrochloric acid, chloride salts, such as ammonium chloride, calcium chloride, ferric chloride, lithium chloride, potassium chloride, sodium chloride, triethylbenzyl ammonium chloride, tetrabutyl ammonium chloride, hydrobromic acid, and bromide salts, such as ammonium bromide, calcium bromide, ferric bromide, lithium bromide, potassium bromide, sodium bromide, triethylbenzyl ammonium bromide, tetrabutyl ammonium bromide, or, in a case wherein the copolymer comprises a chloride or bromide counterion, the chloride or bromide counterion of the copolymer. In one embodiment, the source of chloride ions comprises lithium chloride.

In one embodiment, the source of chloride or bromide ions comprises silver chloride and/or silver bromide, which may be added to the reaction mixture in the form of colloidal particles. The colloidal particles of silver chloride and/or silver bromide may have a particle size of from about 10 nm to about 10 μm, more typically of from about 50 nm to about 10 μm.

The pH of the at least one polyol may be any pH at room temperature (25° C.). The pH of the at least one polyol may be determined by conventional analytical methods known in the art, including, for example, colorimetric titration, potentiometric titration, direct measurement using a pH meter, and the like. Typically, the pH of the at least one polyol is from about 1 to about 14. More typically, the pH of the at least one polyol is from about 5 to about 12. Even more typically, the pH of the at least one polyol is from about 7 to about 10.

The at least one base is any compound that increases the pH of the reaction mixture in which the at least one base is dissolved, dispersed, or suspended. Suitable bases include alkali metal hydroxides, such as, for example, sodium hydroxide, lithium hydroxide, potassium hydroxide, rubidium hydroxide, cesium hydroxide, and mixtures thereof. In an embodiment, the at least one base comprises sodium hydroxide, lithium hydroxide, potassium hydroxide, or mixtures thereof.

The amount of the at least one base is typically from about 5.39×10⁻⁵ to about 3.47×10⁻⁴ pbw of the at least one base per 1 pbw of the total amount of the at least one polyol used in the reaction. More typically, the amount of the at least one base is typically from about 5.39×10⁻⁵ to about 1.30×10⁻⁴ pbw of the at least one base per 1 pbw of the total amount of the at least one polyol used in the reaction.

The total amount of silver compound added to the reaction mixture over the entire course of the reaction, based on one liter of reaction mixture, is typically from about 1.5×10⁻³ mole to about 1 mole of the silver compound (corresponding, in the case of AgNO₃ as the silver compound and ethylene glycol as the polyol, to about 0.026 wt % to about 17 wt % AgNO₃ in ethylene glycol), more typically from greater than or equal to 3 x10⁻² mole to about 1 mole of the silver compound (corresponding, in the case of AgNO₃ as the silver compound and ethylene glycol as the polyol, to about 0.51 wt % to about 17 wt % AgNO₃ in ethylene glycol). The silver compound may be introduced to the reaction mixture as a solid powder, the total amount of which may be introduced at one time or which may introduced in a series of portion of the total amount. Alternatively, the silver compound may be fed to the reaction mixture as a dilute solution of the silver compound in the polyol comprising from about 10 g to about 100 g of the silver compound per 1000 g polyol at a rate that is sufficiently slow as to avoid reducing the temperature of the reaction mixture.

In one embodiment, the total amount of silver compound added to the reaction mixture is, based on one Liter of reaction mixture, typically from about 0.02 moles to about 0.22 moles (corresponding, in the case of AgNO₃ as the silver compound and ethylene glycol as the polyol, to from about 0.3 wt % to about 3.75 wt % AgNO₃ in ethylene glycol), more typically from about 0.06 moles to about 0.18 moles (corresponding, in the case of AgNO₃ as the silver compound and ethylene glycol as the polyol, to from about 1 wt % to 3 wt % AgNO₃ in ethylene glycol), even more typically from about 0.07 moles to about 0.18 moles (corresponding, in the case of AgNO₃ as the silver compound and ethylene glycol as the polyol, to from about 1.25 wt % to about 3 wt % AgNO₃ in ethylene glycol). In one embodiment, the total amount of silver compound added to the reaction mixture is, based on one Liter of reaction mixture, from greater than 0.1 moles to about 0.22 moles (corresponding, in the case of AgNO₃ as the silver compound and ethylene glycol as the polyol, to from about 1.7 wt % to about 3.75 wt % AgNO₃ in ethylene glycol).

In one embodiment, the nanostructures are made in the presence of from about 5.4×10⁻⁵ moles to about 5.4×10⁻³ moles of particles of silver chloride and/or particles of silver bromide per Liter of reaction mixture. While not wishing to be bound by theory, it is believed that the particles of silver chloride and/or particles of silver bromide catalyze growth of the silver nanostructures, but do not participate as a reactive “seeds” that become incorporated within the silver nanostructures.

In one embodiment, the at least one polyol and at least one silver compound are reacted at a temperature of from about 100° C. to about 210° C., more typically from about 130 to about 185° C.

In one embodiment, at least a portion of the polyol is preheated to a temperature of from about 100° C. to about 210° C., more typically from about 130° C. to about 185° C., typically for a period of greater than about 1 minute, more typically for a period of greater than about 5 minutes prior to introduction of the source of chloride or bromide ions, and/or the silver compound.

In one embodiment, particles of silver chloride or silver bromide are formed in the polyol in a preliminary step, wherein a silver compound and polyol are reacted in the presence of a source of chloride or bromide ions, typically in with the silver compound in an excess of from greater than 1, more typically from about 1.01 to about 1.2 moles, of silver compound per mole chloride or bromide ions. In one embodiment, from about 5.4×10⁻⁵ to about 5.4×10⁻⁴ moles silver compound per liter of reaction mixture are reacted in the presence of from about 5.4×10⁻⁵ to about 5.4×10⁻⁴ moles of the source of chloride and/or bromide ions per liter of reaction mixture to form silver chloride and/or silver bromide seed particles in the reaction mixture. In one embodiment particles of silver chloride or silver bromide are formed at a temperature of from about 100° C. to about 210° C., more typically from about 130° C. to about 185° C. The formation of the silver chloride or silver bromide particles is typically conducted over a time period of greater than or equal to about 1 minute, more typically of from about 1 minute to about 10 minutes.

In one embodiment from about 1.5×10⁻³ to about 1 mole of the silver compound per Liter of reaction mixture are added in a second reaction step. The growth step is conducted at a temperature of about 100° C. to about 210° C., more typically from about 130° C. to about 185° C. The second reaction step of the reaction is typically conducted over a time period of greater than or equal to about 5 minutes, more typically from about 5 minutes to about 4 hours, and even more typically from about 10 minutes to 1 about hour.

In one embodiment, particles of silver chloride or silver bromide are formed in the polyol simultaneously with the formation of the silver nanostructures in a single step, wherein a silver compound and polyol are reacted in the presence of a source of chloride or bromide ions, typically in with the silver compound in very large molar excess. The single step formation reaction is conducted at a temperature of from about 100° C. to about 210° C., more typically from about 130° C. to about 185° C. The single step formation reaction is typically conducted over a time period of greater than or equal to about 5 minutes, more typically from about 5 minutes to about 4 hours, and even more typically from about 10 minutes to about 1 hour.

The reaction may be conducted under an air atmosphere or under an inert atmosphere, such as a nitrogen or argon atmosphere. In one embodiment, the reaction is conducted under a nitrogen atmosphere.

The copolymer is believed to function as an organic protective agent. The amount of copolymer is typically from about 0.1 to about 20 parts by weight (“pbw”), more typically from about 1 to about 5 pbw, of the copolymer per 1 pbw of silver compound, based on the total amount of the silver compound added to the reaction mixture.

In one embodiment, the reaction is conducted in the presence of, based on the weight of the reaction mixture, from about 0.01 wt % to about 50 wt %, more typically from about 0.1 wt % to about 20 wt %, and even more typically from about 0.5 wt % to 8 wt %, of the copolymer.

In one embodiment, the at least one silver compound comprises silver nitrate, the at least one polyol comprises ethylene glycol, the total amount of silver nitrate added to the reaction mixture is from 1.5×10⁻³ mole to about 1 mole silver nitrate per Liter of reaction mixture, and the reaction is conducted in the presence of, based on the weight of the reaction mixture, from about 0.01 wt % to about 50 wt %, more typically from about 0.1 wt % to about 20 wt %, and even more typically from about 0.5 wt % to 8 wt %, of the copolymer.

Saturated or unsaturated five-, six-, or seven-membered acylamino- or diacylamino-containing heterocylic ring moieties suitable as the at least one pendant group of the first constitutional repeating unit of the copolymer include, for example, pyrrolidonyl, pyrrolidinedionyl, azacyclohexanoyl, azacyclohexadionyl, azacycloheptanonyl, and azacycloheptadionyl.

In one embodiment, the first constitutional repeating units of the copolymer each independently comprise a pyrrolidonyl moiety or a pyrrolidinedionyl moiety. In one embodiment, each of the first constitutive units of the copolymer comprises a pyrrolidonyl moiety.

In one embodiment, the first constitutional repeating units each independently comprise a pendant group according to structure (I):

R¹—R²—  (I)

wherein:

-   -   R¹ is a saturated or unsaturated five-, six-, or seven-membered         acylamino- or diacylamino-containing heterocylic ring moiety,         more typically pyrrolidonyl, 2,5 pyrrolidinedionyl,         azacyclohexanonyl, azacyclohexadionyl azacycloheptanonyl,         azacycloheptadionyl, even more typically pyrrolidonyl or 2,5         pyrrolidinedionyl, and     -   R² is divalent linking group, more typically a divalent linking         group selected from poly(alkyleneoxy), —O—C(O)—, —NH—C(O)— and         —(CH₂)_(n)—, wherein n is an integer of from 1 to 10, more         typically of from 1 to 3, or is absent.

The first constitutional repeating units may be made by known synthetic techniques, such as, for example, by grafting of one or more five-, six-, or seven-membered saturated or unsaturated acylamino- or diacylamino-containing heterocylic ring moieties onto a polymer backbone, such as a hydrocarbon polymer backbone, a polyester polymer backbone, or a polysaccharide polymer backbone, or by copolymerization of a nonionic monomer, as described below, with, for example, an ionic monomer, as described below.

In one embodiment, the first constitutional repeating units of the copolymer of the present invention are derived from a first monomer comprising at least one reactive functional group and at least one five-, six-, or seven-membered saturated or unsaturated acylamino- or diacylamino-containing heterocylic ring moiety per molecule of the monomer.

Suitable reactive functional groups include, for example, hydroxyl groups, isocyanate groups, epoxide groups, amino groups, carboxylate groups, and α,β-unsaturated groups, such as —CH₂═CH₂, or —H(CH₃)C═CH₂.

In one embodiment, the first monomer comprises one or more compounds according to structure (II):

R¹—R²—R³   (II)

wherein:

-   -   R¹ and R² are as described above, and     -   R³ is a reactive functional group, more typically a reactive         group selected from —CH₂═CH₂, and —H(CH₃)C═CH₂.

In one embodiment, the first constitutional repeating units of the copolymer of the present invention are derived from a first monomer selected from vinyl pyrrolidone. vinyl caprolactam, and mixtures thereof. More typically, each of the first constitutional repeating units of the copolymer of the present invention is derived from vinylpyrrolidone.

Constitutional repeating units suitable as the second constitutional repeating units of the copolymer of the present invention may be any constitutional repeating units that differ in composition from the first constitutional repeating units.

In one embodiment, the second constitutional repeating units each comprise at least one pendant moiety per second constitutional repeating unit that: (i) is selected from ionic organic moieties and nonionic organic moieties, and (ii) is not a saturated or unsaturated, five-, six-, or seven-membered, acylamino- or diacylamino-containing heterocylic ring moiety.

In one embodiment, the second constitutional repeating units each comprise at least one pendant moiety per second constitutional repeating unit that is selected from ionic organic moieties. Suitable ionic organic moieties include cationic moieties, anionic moieties, and amphoteric/zwitterionic moieties.

In one embodiment, one or more of the second constitutional repeating units comprise at least one pendant cationic moiety.

Suitable cationic moieties include nitrogenous organic moieties that comprise a primary, secondary, or tertiary amino nitrogen atom, or a quaternary nitrogen atom. In those embodiments comprising a quaternary nitrogen atom, the, the cationic moiety is typically in the form of a salt that is associated with a counter anion, which may be selected from organic anions, such as sulphonate anions, and inorganic anions, such as halogen anions or nitrate anions. In one embodiment, one or more of the second constitutional repeating units each comprise at least one pendant cationic moiety that comprises a quaternary ammonium nitrogen atom and counter anion, more typically a chloride, bromide, or nitrate counter anion, or a mixture thereof.

In one embodiment, one or more of the second constitutional repeating units each independently comprise, per second constitutional repeating unit, selected from:

-   -   acyclic groups that comprise at least one primary, secondary, or         tertiary amino nitrogen atom or quaternary nitrogen atom per         group, and     -   five or six-membered heterocylic ring-containing groups that         comprise at least one nitrogen atom, which may be a quaternary         nitrogen atom, as a ring member.

Five or six-membered heterocylic ring-containing groups suitable as the at least one nitrogenous cationic group of the second constitutive unit, include, for example, pyrrolidinyl, pyrrolinyl, imidazolidinyl, pyrrolyl, imidazolyl, pyrazolidinyl, pyrazolinyl, piperidinyl, piperazinyl, pyridinyl, pyrazinyl, pyrimadinyl, or pyridazinyl groups, more typically quaternized pyrrolidinyl, quaternized pyrrolinyl, quaternized imidazolidinyl, quaternized pyrrolyl, quaternized imidazolyl, quaternized pyrazolidinyl, quaternized pyrazolinyl, quaternized piperidinyl, quaternized piperazinyl, quaternized pyridinyl, quaternized pyrazinyl, quaternized pyrimadinyl, or quaternized pyridazinyl groups.

In one embodiment, one or more of the second constitutional repeating units comprise at least one pendant anionic organic moiety. Suitable anionic moieties include, for example, carboxylate, sulphonate, sulfate, phosphate, and phosphonate moieties, such as, for example, alkyl carboxylate moieties, alkyl sulphonate moieties, alkaryl sulphonate moieties, and alkyl sulfate moieties, and salts thereof. In some embodiments, the anionic moiety is in the form of a salt that is associated with a counter cation, which may be an inorganic cation or an organic cation, such as an ammonium cation, a cation comprising a primary, secondary, or tertiary amino nitrogen, a cation comprising a quaternary nitrogen atom, an alkali metal cation, or a mixture thereof.

In one embodiment, one or more of the second constitutional repeating units comprise at least one pendant amphoteric/zwitterionic organic moiety. Suitable amphoteric/zwitterionic organic moieties include, for example, moieties that comprise both a cationic group, such as a quaternary nitrogen atom, and anionic group, such as a sulphonate group or a carboxylate group, each of which may independently be in the form of a salt associated with an oppositely charged counterion, as part of the same moiety, such as, for example, sulfobetaine moieties or carboxybetaine moieties.

In one embodiment, one or more of the second constitutional repeating units each independently comprise at least one pendant nonionic organic moiety. Suitable nonionic moieties include hydrocarbyl moieties, such as alkyl, cycloalkyl, aryl, alkaryl, and aralkyl moieties, hydroxyalkyl moieties, and poly(alkylene oxide) moieties.

In one embodiment, the ionic moiety of the ionic constitutional repeating units each independently comprise an acyclic group that comprises at least one quaternized nitrogen atom, such as a moiety according to formula (III):

R²⁰—R²¹—  (III)

wherein:

-   -   R²⁰ is an ionic organic moiety or a nonionic organic moiety that         is not a saturated or unsaturated, five-, six-, or         seven-membered, acylamino- or diacylamino-containing heterocylic         ring moiety, and     -   R²¹ is divalent linking group, more typically a divalent linking         group selected from poly(alkyleneoxy), —O—C(O)—, —NH—C(O)— and         —(CH²)_(m)—, wherein m is an integer of from 1 to 10, more         typically of from 1 to 3, or is absent.

In one embodiment, the copolymer comprises one or more second constitutional repeating units that comprise at least one cationic moiety per such unit. In one embodiment, the copolymer comprises one or more second constitutional repeating units that each independently comprise at least one anionic moiety per such unit. In one embodiment, the copolymer comprises one or more second constitutional repeating units that each independently comprise at least one amphoteric/zwitterionic moiety per such unit. In one embodiment, the copolymer comprises one or more second constitutional repeating units that each independently comprise at least one nonionic moiety per such unit. In one embodiment, the copolymer comprises one or more second constitutional repeating units that each independently comprise at least one cationic moiety per such unit and one or more second constitutional repeating units that each independently comprise at least one anionic moiety per such unit. In one embodiment, the copolymer comprises one or more second constitutional repeating units that each independently comprise at least one cationic moiety per such unit and one or more second constitutional repeating units that each independently comprise at least one amphoteric/zwitterionic moiety per such unit. In one embodiment, the copolymer comprises one or more second constitutional repeating units that each independently comprise at least one cationic moiety per such unit and one or more second constitutional repeating units that each independently comprise at least one nonionic moiety per such unit. In one embodiment, the copolymer comprises one or more second constitutional repeating units that each independently comprise at least one anionic moiety per such unit and one or more second constitutional repeating units that each independently comprise at least one amphoteric/zwitterionic moiety per such unit. In one embodiment, the copolymer comprises one or more second constitutional repeating units that each independently comprise at least one anionic moiety per such unit and one or more second constitutional repeating units that each independently comprise at least one nonionic moiety per such unit. In one embodiment, the copolymer comprises one or more second constitutional repeating units that each independently comprise at least one amphoteric/zwitterionic moiety per such unit and one or more second constitutional repeating units that each independently comprise at least one nonionic moiety per such unit.

The second constitutional repeating units may be made by known synthetic techniques, such as, for example, by grafting of ionic or nonionic organic moieties onto a polymer backbone, such as a hydrocarbon polymer backbone, a polyester polymer backbone, or a polysaccharide polymer backbone, or by copolymerization of a second monomer, as described below, with, for example, the above-described first monomer.

In one embodiment, the second constitutional repeating units of the copolymer of the present invention are derived from a second monomer that is copolymerizable with the first monomer and comprises, per molecule of the monomer, at least one reactive functional group and at least one nitrogenous cationic group selected from:

-   -   acyclic groups that comprise at least one primary, secondary, or         tertiary amino nitrogen atom or quaternary nitrogen atom per         group, and     -   five or six-membered heterocylic ring-containing groups that         comprise at least one nitrogen atom, which may be a quaternary         nitrogen atom, as a ring member, such as, for example,         pyrrolidinyl, pyrrolinyl, imidazolidinyl, pyrrolyl, imidazolyl,         pyrazolidinyl, pyrazolinyl, piperidinyl, piperazinyl, pyridinyl,         pyrazinyl, pyrimadinyl, or pyridazinyl moiety.

In one embodiment, the acyclic groups that comprise at least one primary, secondary, or tertiary amino nitrogen atom or quaternary nitrogen atom per group is a an acyclic moiety that is cyclizable, either simultaneously with or subsequent to copolymerization with the first monomer, to form a five or six-membered heterocylic ring that comprises at least one nitrogen atom, which may be a quaternary nitrogen atom, as a ring member.

In one embodiment, the second constitutional repeating units of the copolymer of the present invention are derived from a second monomer comprising, per molecule of the monomer, at least one reactive functional group and at least one group that is (i) selected from ionic organic moieties and nonionic organic moieties, and (ii) is not a saturated or unsaturated, five-, six-, or seven-membered, acylamino- or diacylamino-containing heterocylic ring moiety.

Suitable reactive functional groups are those described above in regard to the first monomer.

In one embodiment, the first monomer comprises one or more compounds according to structure (IV):

R²⁰—R²¹—R²²   (IV)

wherein:

-   -   R²⁰ and R²¹ are each as described above, and     -   R²² is a reactive functional group, more typically a reactive         group selected from —CH₂═CH₂, and —H(CH₃)C═CH₂.

Suitable cationic monomers include, for example, dimethylaminomethyl (meth)acrylate, dimethylaminopropyl (meth)acrylate, di(t-butyl)aminoethyl (meth)acrylate, dimethylaminomethyl (meth)acrylamide, dimethylaminoethyl (meth)acrylamide, dimethylaminopropyl (meth)acrylamide, vinylamine, vinyl imidazole, vinylpyridine, vinylpyrrolidine, vinylpyrroline, vinylpyrazolidine, vinylpyrazoline, vinylpiperidine, vinylpiperazine, vinylpyridine, vinylpyrazine, vinylpyrimadine, vinylpyridazine, trimethylammonium ethyl (meth)acrylate salts, dimethylammonium ethyl (meth)acrylate salts, dimethylbenzylammonium (meth)acrylate salts, benzoylbenzyl dimethylammonium ethyl(meth) acrylate salts, trimethyl ammonium ethyl (meth)acrylamido salts, trimethyl ammonium propyl (meth)acrylamido salts, vinylbenzyl trimethyl ammonium salts, diallyldimethyl ammonium salts.

In one embodiment, the second constitutional repeating units of the copolymer of the present invention are derived from a cationic monomer selected from diallyldimethylammonium salts, such as diallyldimethylammonium nitrate, quaternized dimethylaminoethyl(meth)acrylate salts, such as quaternized dimethylaminoethyl(meth)acrylate nitrate, and quaternized vinylimidazole salts, such as quaternized vinylimidazole nitrate.

Suitable anionic monomers include, for example, acrylic acid, acrylic acid, methacrylic acid, vinyl sulphonic acid, vinylbenzene sulphonic acid, (meth)acrylamidomethylpropane sulphonic acid, 2-sulphoethyl methacrylate, and styrenesulfonate, as well as mixtures of and salts thereof.

Suitable amphoteric/zwitterionic monomers include, for example, sulfobetaine (meth)acrylates, sulfobetaine (meth)acrylamides, sulfobetaine (meth)allyl compounds, sulfobetaine vinyl compounds, carboxybetaine (meth)acrylates, carboxybetaine (meth)acrylamides, caboxybetaine (meth)allyl compounds and carboxybetaine vinyl compounds, such as for example, N-(3-sulfopropyl)-N-(methacryloxyethyl)-N,N-dimethyl ammonium betaine, N-(3-acrylamidopropyl)-N,N-dimethylammonioacetate, or N-(3-acryloamidopropyl)-N,N-dimethyl-N-(carboxymethyl)ammonium bromide.

Suitable nonionic monomers include, for example, (meth)acrylamide, esters of an monoethylenically unsaturated monocarboxylic acids, such as methyl (meth)acrylate, ethyl (meth)acrylate, n-propyl (meth)acrylate, n-butyl(meth)acrylate, 2-ethyl-hexyl (meth)acrylate, or hydroxyalkyl esters such as 2-hydroxyethyl (meth)acrylate, polyethylene and/or polypropylene oxide (meth)acrylates (i.e. polyethoxylated and/or polypropoxylated (meth)acrylic acid), vinyl alcohol, vinyl acetate, vinyl versatate, vinyl nitriles, acrylonitrile, vinyl aromatic compounds, such as styrene, and mixtures thereof.

In one embodiment, the copolymer comprises, based on 1000 constitutional repeating units:

-   -   from 500 to 999, more typically from 800 to 999, even more         typically from 900 to 990, first constitutional repeating units,         and     -   from 1 to 500, more typically from 1 to 200, even more typically         from 10 to 100 second constitutional repeating units.

In one embodiment, the copolymer is made by copolymerizing a mixture of monomers that comprises more first monomers and one or more second monomers that each independently comprise at least one cationic moiety per molecule of such monomer. In one embodiment, the copolymer is made by copolymerizing a mixture of monomers that comprises one or more first monomers and one or more second monomers that each independently comprise at least one anionic moiety per molecule of such monomer. In one embodiment, the copolymer is made by copolymerizing a mixture of monomers that comprises one or more first monomers and one or more second monomers that each independently comprise at least one amphoteric/zwitterionic moiety per molecule of such monomer. In one embodiment, the copolymer is made by copolymerizing a mixture of monomers that comprises one or more first monomers and one or more second monomers that each independently comprise at least one nonionic moiety per molecule of such monomer. In one embodiment, the copolymer is made by copolymerizing a mixture of monomers that comprises one or more first monomers, one or more second monomers that each independently comprise at least one cationic moiety per molecule of such monomer, and one or more second monomers that each independently comprise at least one anionic moiety per molecule of such monomer. In one embodiment, the copolymer is made by copolymerizing a mixture of monomers that comprises one or more first monomers, one or more second monomers that each independently comprise at least one cationic moiety per molecule of such monomer, and one or more second monomers that each independently comprise at least one amphoteric/zwitterionic moiety per molecule of such monomer. In one embodiment, the copolymer is made by copolymerizing a mixture of monomers that comprises one or more first monomers, one or more second monomers that each independently comprise at least one cationic moiety per molecule of such monomer, and one or more second monomers that each independently comprise at least one nonionic moiety per molecule of such monomer. In one embodiment, the copolymer is made by copolymerizing a mixture of monomers that comprises one or more first monomers, one or more second monomers that each independently comprise at least one anionic moiety per molecule of such monomer, and one or more second monomers that each independently comprise at least one amphoteric/zwitterionic moiety per molecule of such monomer. In one embodiment, the copolymer is made by copolymerizing a mixture of monomers that comprises one or more first monomers, one or more second monomers that each independently comprise at least one anionic moiety per molecule of such monomer, and one or more second monomers that each independently comprise at least one nonionic moiety per molecule of such monomer. In one embodiment, the copolymer is made by copolymerizing a mixture of monomers that comprises one or more first monomers, one or more second monomers that each independently comprise at least one amphoteric/zwitterionic moiety per molecule of such monomer, and one or more second monomers that each independently comprise at least one nonionic moiety per molecule of such monomer.

In one embodiment, the copolymer is made by copolymerizing a mixture of monomers, comprising, based on 1000 moles of such monomers:

-   (a) from 800 to 999 moles of one or more first monomers, each     independently comprising at least one reactive functional group per     molecule and at least one pendant saturated or unsaturated, five-,     six-, or seven-membered acylamino- or diacylamino-containing     heterocylic ring moiety per molecule, and -   (b) from 1 to 200 moles of one or more second monomers, each     independently comprising at least one reactive functional group per     molecule and at least one pendant organic moiety that comprises at     least one primary, secondary, or tertiary amino nitrogen atom or     quaternary nitrogen atom per molecule.

The copolymer of the present invention typically has weight average molecular weight of greater than or equal to 5,000 grams per mole (g/mol), more typically, a weight average molecular weight of from about 10,000 to about 2,000,000 g/mol, even more typically from about 10,000 to about 500,000 g/mol, and still more typically from about 10,000 to about 100,000 g/mol.

In one embodiment, the copolymer is a random copolymer, comprising chains of randomly arranged first constitutional repeating units and second constitutional repeating units. In one embodiment, the copolymer is a block copolymer, comprising blocks of two or more consecutive first constitutional repeating units and blocks of two or more consecutive second constitutive units.

Methods for making suitable copolymers are known in the art. In one embodiment, the polymer according to the present invention is made by copolymerization of ethylenically unsaturated monomers according to known free radical polymerization processes. In one embodiment, the copolymer is made by a controlled free radical polymerization techniques, such as the known controlled free radical polymerization processes of atom transfer radical polymerization (“ATRP”), reversible addition fragmentation transfer (“RAFT” polymerization), or macromolecular design via interchange of xanthates (“MADIX” polymerization).

If the second monomer comprises a reactive group that is cyclizable to form a five or six-membered heterocylic ring that comprises at least one quaternized or quaternizable nitrogen atom as a ring member, the cyclization to form the heterocylic ring structure may be conducted simultaneously with the copolymerization with the first monomer, such as by, for example, simultaneous polymerization and cyclization of a quaternized or quaternizable nitrogen atom-containing diallyl monomer, or conducted subsequent to such polymerization.

If the second monomer comprises a quaternizable nitrogen atom as a ring member, then the nitrogen may be quaternized subsequent to the polymerization reaction.

In one embodiment, the copolymer is a random copolymer made by free radical polymerization of vinyl pyrrolidone, vinyl caprolactam, or vinyl pyrrolidone and vinyl caprolactam with one or more ethylenically unsaturated cationic monomers.

In one embodiment, the copolymer is a random copolymer made by free radical polymerization of a monomer mixture comprising from about 80 pbw to less than 100 pbw, more typically from about 90 pbw to about 99 pbw, of vinyl pyrrolidone and from greater than 0 to about 20 pbw, more typically from about 1 to about 10 pbw, of a diallyldimethylammonium salt.

In one embodiment, the at least one silver compound comprises silver nitrate, the at least one polyol comprises ethylene glycol, the total amount of silver nitrate added to the reaction mixture is from 1.5×10⁻³ mole to about 1 mole silver nitrate per Liter of reaction mixture, the reaction is conducted in the presence of, based on the weight of the reaction mixture, from about 0.01 wt % to about 50 wt %, more typically from about 0.1 wt % to about 20 wt %, and even more typically from about 0.5 wt % to 8 wt %, of a random copolymer made by free radical polymerization of a monomer mixture comprising from about 80 pbw to less than 100 pbw, more typically from about 90 pbw to about 99 pbw, of vinyl pyrrolidone and from greater than 0 to about 20 pbw, more typically from about 1 to about 10 pbw, of a diallyldimethylammonium salt.

The process of the present invention typically produces a high yield of silver nanowires. In one embodiment, greater than or equal to 70 wt % of silver feed is converted to nanowires and less than 30 wt % of silver feed is converted to isotropic nanostructures, more typically greater than or equal to 80 wt % of silver feed is converted to nanowires and less than 20 wt % of silver feed is converted to isotropic nanoparticles, and even more typically more than 90 wt % of silver feed is converted to nanowires and less than 10 wt % of silver feed is converted to isotropic nanostructures. In one embodiment, greater than or equal to 99 wt % of silver feed is converted to nanowires and less than 1 wt % of silver feed is converted to isotropic nanostructures.

In one embodiment, the silver nanostructures comprise elongated silver nanostructures, known as “silver nanowires” having a diameter of from about 10 nm to about 2 μm, more typically from about 10 nm to about 150 nm, even more typically from about 10 nm to about 60 nm, and a length of from about 5 μm to about 300 μm, more typically from about 10 to about 200 μm.

In one embodiment, the silver nanostructures comprise silver nanowires having a diameter of from about 10 nm to about 150 nm, even more typically from about 10 nm to about 60 nm, and an aspect ratio, that is, a length to diameter ratio, of greater than 100, or greater than 150, or greater than 200, or greater than 300.

In one embodiment, the nanowires made by the process of the present invention exhibit an aspect ratio that is, on average, greater than that of nanowires made by an analogous product wherein poly(vinyl pyrrolidone) is substituted for the copolymer component of the process of the present invention. In one embodiment, the nanowires made by the process of the present invention exhibit an aspect ratio that is, on average, greater than that of nanowires made by an analogous product wherein poly(vinyl pyrrolidone is substituted for the copolymer component of the process of the present invention by a factor of a least 2, more typically by a factor of at least 3.

The product mixture comprises polyol, copolymer, and silver nanostructures, wherein the silver nanostructures comprise silver nanowires and may comprise silver nanostructures other than silver nanowires, such as, isotropic silver particles.

The silver nanostructures may be isolated from the polyol and copolymer components of the product mixture by, for example, gravity separation, centrifugation, or filtration. In one embodiment, the silver nanostructures are then washed in water, an alcohol, typically a (C₁-C₃)alkanol, or a mixture of water and alkanol, to remove residues of the polyol and copolymer from the isolated nanowires.

Silver nanowires produced by the process of the present invention may be separated from other non-nanowire silver nanostructure components that may be present in the product mixture by dispersing the silver nanostructures in a polar aprotic organic liquid, such as acetone or acetonitrile, followed by isolation of the nanowires from the liquid by gravity separation or centrifugation. The silver nanowires tend to agglomerate and precipitate from the polar aprotic liquid, while isotropic silver nanostructures tend to remain suspended in the polar aprotic organic liquid.

In one embodiment, the product mixture is subjected to gravity separation, the silver nanowire fraction of the separated product mixture is re-dispersed in acetone and subjected to gravity separation and the silver nanowire fraction of the separated acetone dispersion is the re-dispersed in water, alcohol or a mixture thereof.

The residue of the copolymer used in the process of the present invention is more easily cleaned from the silver nanostructure product than the poly(vinylpyrrolidone) homopolymer of prior art processes, which typically require multiple iterations of water or water and alcohol washing to remove from the silver nanostructure product. For example, the copolymer residue may typically be removed from the silver nanostructures in a single water/alkanol washing step, while removal of poly(vinyl pyrrolidone homopolymer residue from silver nanostructures typically requires form 5 to 10 iterations of an analogous water/alkanol washing step. Reducing the amount of or eliminating the copolymer or homopolymer from the dispersion of silver nanowires is of great benefit in using the silver nanowires to easily make electrically conductive polymer films having very high conductivity. The silver nanowires of the dispersion of the present invention can be used to make polymer films having high electrical conductivity without requiring the extra steps required by prior art processes, such as iterative washing steps or heat treating or heating and compressing the silver nanowire network to displace a coating of vinylpyrrolidone residue from the surfaces of the nanowires and allow metal to metal contact between the nanowires of the network.

In one embodiment, silver nanowires are provided in the form of a dispersion comprising silver nanowires dispersed in liquid medium comprising water, a (C₁-C₆)alkanol, or a mixture thereof. Including an alkanol component in the liquid medium of the dispersion is of benefit in reducing oxidation of the silver nanostructure component of the dispersion.

In one embodiment, the nanowire dispersion comprises silver nanowires dispersed in aqueous medium wherein the dispersion comprises less than 100 pbw, or less than 10 pbw, or less than 5 pbw or less than 1 pbw of the copolymer per 1,000,000 pbw of silver nanowires. In one embodiment, the dispersion comprises no detectable amount of the copolymer.

The silver nanowires made by the process of the present invention are useful in combination with an electrically conductive polymer, as a component of an electrically conductive film. Suitable electrically conductive polymers include electrically conductive polythiophene polymers, electrically conductive poly(selenophene) polymers, electrically conductive poly(telurophene) polymers, electrically conductive polypyrrole polymers, electrically conductive polyaniline polymers, electrically conductive fused polycylic heteroaromatic polymers, and blends of any such polymers. In one embodiment, the electrically conductive polymer comprises a doped electrically conductive polymer known as PEDT:PSS, which comprises poly(3,4-ethylenedioxythiophene or “PEDOT” and a water soluble polymeric acid dopant comprising a poly(styrene sulfonic acid) or “PSS”. Such electrically conductive polymer films typically exhibit high conductivity and high optical transparency and are useful as a layer in an electronic device. Suitable electronic devices include any device that comprises one or more layers of semiconductor materials and makes use of the controlled motion of electrons through such one or more layers, such as, for example: devices that converts electrical energy into radiation, such as, for example, light-emitting diodes, light emitting diode displays, diode lasers, or lighting panels, devices that detect signals through electronic processes, such as, for example, photodetectors, photoconductive cells, photoresistors, photoswitchs, phototransistors, phototubes, infrared (“IR”) detectors, or biosensors, devices that convert radiation into electrical energy, such as, for example, photovoltaic devices or solar cells, and devices that includes one or more electronic components with one or more semiconductor layers, such as, for example, transistors or diodes.

In one embodiment, the process of the present invention permits the use of a higher concentration of silver compound, for example silver nitrate, in the reaction mixture which enables production of a product mixture having a higher concentration of silver nanostructures, more typically silver nanowires, than an analogous process wherein poly(vinyl(pyrrolidone) homopolymer is used in place of the copolymer component of the process of the present invention.

In one embodiment, the process of the present invention enables production of silver nanowires having a higher aspect ratio than silver nanowires made by an analogous process wherein poly(vinyl(pyrrolidone) homopolymer is used in place of the copolymer component of the process of the present invention.

In general, silver nanostructures made by the process of the present invention are more easily cleaned than silver nanostructures made by an analogous process wherein poly(vinyl(pyrrolidone) homopolymer is used in place of the copolymer component of the process of the present invention, because residues of the copolymer component of the process of the present invention is more easily removed from silver nanowires structures than are residues of poly(vinyl pyrrolidone) homopolymer.

EXAMPLES 1A-1E AND COMPARATIVE EXAMPLE C1

The poly(vinylpyrrolidone-co-diallyldimethylammonium nitrate) random copolymers (“poly(VP-co-DADMAN”) of Examples 1A-1E were each made by copolymerizing vinylpyrrolidone monomer with diallyldimethylammonium nitrate monomer (“DADMAN”).

DADMAN monomer was made by exchanging the chloride counter ion of diallyldimethylammonium chloride monomer (“DADMAC”, shown in structure (b) above) with nitrate counter ions, using silver nitrate, according to reaction:

C₈H₁₆N⁺Cl⁻+AgNO₃→AgCl+C₈H₁₆N⁺NO₃.

The exchange of chloride for nitrate ions was done by adding the adequate amount of a solution of silver nitrate in water (1:1 molar ratio between Cl⁻ and NO₃ ⁻) into X/0.6 g of a solution of 60 wt % DADMAC in water, where X=1, 2, 4, 8, or 16.

The exchanges each occurred quickly and produced a white silver chloride precipitate that was easily separated from the DAMAN monomer product solutions by centrifugation (5 min at 2000 rpm). The precipitates were washed one time with 5 ml of water and centrifuged again in order to retrieve all the monomer. The total exchanged monomer solutions were then filtered with a 0.2 μm filter prior to use in copolymerization reactions, as described below.

VP and DADMAN monomers were copolymerized according to the general Scheme A below, using controlled radical polymerization using azobisisobutyronitrile (AlBN) as the polymerization initiator and a thiocarbonylthio transfer agent, to produce a linear poly(VP-co-DADMAN) copolymer.

In a 500 ml jacketed reactor, 90 g of vinylpyrrolidone (VP), 0.2 ml of the thiocarbonylthio transfer agent and an aqueous DADMAN solution were heated to 68° C. under nitrogen. A solution of 0.5 g of AlBN in 10 g of VP was then added stepwise in the solution, according to the following schedule:

-   -   at t=0, 2 ml of the AlBN/VP solution was added to the solution,     -   at t=20 min, the temperature had increased to about 75° C., due         to exothermic polymerization reaction, and 0.5 ml of AlBN/VP         solution were added, and     -   at t=55 min, the temperature in the reactor was about 78° C.,         150 ml of water pre-heated to 68° C. were added to the reaction         mixture with the rest of the AlBN/VP solution.

Following addition of the water and final AlBN/VP solution, the reaction mixture was kept at 68° C. for 4 more hours and then allowed to cool at room temperature for another 6 to 10 hours. The viscous product solution so produced was then precipitated in 750 ml of acetone and washed twice with 100 ml aliquots of acetone. The washed product was then dried at 70° C. under vacuum with nitrogen purge for one day, and then ground and dried again before use. The theoretical weight average molecular weight obtained by above described polymerization process is about 100,000 g/mol. The yield of this process was typically about 75%. Representative 1H NMR and FTIR spectra of the copolymer product are shown in FIGS. 1(a) and 1(b).

The poly(vinyl pyrrolidone) homopolymer of Comparative Example C1 was made by a process analogous to that used to make the copolymers of Examples 1A-1E, but using only vinyl pyrrolidone monomer, that is, no DADMAN monomer was included in the reaction mixture.

TABLE I DADMAN Example # content (wt %) C1 0 1A 1 1B 2 1C 4 1D 8 1E 16

EXAMPLES 2A-2G AND COMPARATIVE EXAMPLES C2A-C2C

The silver nanowires of Examples 2A-2G were made according to the general synthesis process described below, wherein the composition of the copolymer and the amount of silver nitrate added to the reaction mixture were varied. In each case, a respective one of the poly(VP-co-DADMAN) copolymers of Example 1A-1E was used as a protectant.

Typically, 35 g of ethylene glycol with 0.0055 g of lithium chloride were heated to 173° C., with nitrogen purge, for 1 hour. The poly(VP-co-DADMAN) copolymer (typically in an amount of 1.5 g) was added at the end of this pre-treatment. A feed solution consisting of a given amount (between 0.3 and 1.5 g) of silver nitrate dissolved in 7.5 g of ethylene glycol was used to introduce silver nitrate and more ethylene glycol into the reaction mixture. In a seeding step, an initial amount of silver nitrate (0.05 g, typically in the form of 0.34 mL of a feed solution containing 1 g of silver nitrate in 7.5 g of ethylene glycol) was then fed into the reaction mixture, upon which the reaction mixture turned brown in color. After 6 minutes, the remainder of the silver nitrate feed solution was added to the reaction mixture using a syringe, at a rate of 1.5 ml/min. As the silver nitrate feed was added, the reaction mixture darkened, turned grey in color, and then, typically within about 7 minutes after the beginning of the addition of the silver nitrate feed, nanowires became visible in the reaction mixture. Depending on the total amount of silver nitrate added, the reaction took from about 15 to about 30 minutes reach completion.

The pH of the ethylene glycol used (high-purity anhydrous ethylene glycol; Sigma-Aldrich Lot SHBB8374V, “Lot A”) in the reaction mixture was determined to be 8.9 by dilution and titration. The pH of the pure ethylene glycol can be read on the vertical axis, for V=0 mL, of the titration curve shown in FIG. 5. Lot A ethylene glycol was used in the present examples 2A-2G and Comparative Examples C2A-C2C as well as following Examples 3 and 4.

The silver nanowires of Comparative Examples C2-A to C2-C were made by an analogous process to that used to make the silver nanowires of Examples 2A-2G, except that poly(VP) homopolymer of Comparative Example C1 was substituted for poly(VP-co-DADMAN) copolymer.

For each synthesis, the reaction was left to react until complete reduction of silver nitrate. The nanowires of Examples 2A-2G were isolated form the reaction mixture by gravity separation and the poly(VP-co-DADMAN residues were removed from the nanowires by washing with a mixture of water and alkanol. The nanowires of Comparative Examples C1-C3 were isolated from the reaction mixture by gravity separation and removal of the poly(VP) residues from the nanowires required multiple (at least 5) iterations of the water/alkanol washing step. In each case, silver nanowires were separated from isotropic silver nanostructures by agglomerating the silver nanowires in a mixture of acetone and water and collecting the agglomerated silver nanowires.

An optical microscope was used to follow the evolution of each reaction and to determine the physical characteristics of the product nanostructures. The polymer or copolymer used in the nanowire synthesis reaction (and in the case of poly(VP-co-DADMAN) copolymers, the DADMAN content of the copolymer) and amount of AgNO₃ used in to make the silver nanowires of Examples 2A-2G and Comparative Examples C2A-C2C and the numerical average length of the respective silver nanowires are summarized in TABLE II below.

TABLE II AgNO₃ Nanowire Nanowire Polymer or Copolymer AgNO₃ Amount length Ex# used in synthesis Ex # (wt %) (g) (μm) 2A 1A (1 wt % DADMAN) 1.25 0.5 15 2B 1A (1 wt % DADMAN) 2.5 1 25 2C 1B (2 wt % DADMAN) 2.5 1 16 2D 1B (2 wt % DADMAN) 2.9 1.16 18 2E 1D (8 wt % DADMAN) 1.25 0.5 5 2F 1D (8 wt % DADMAN) 2.5 1 20 2G 1D (8 wt % DADMAN) 3.75 1.5 27 C2A C1 (poly(VP) 1 0.4 10 homopolymer) C2B C1 (poly(VP) 1.25 0.5 12 homopolymer) C2C C1 (poly(VP) 2.5 1 produced an homopolymer) agglomerate of unrecoverable nanostructures

The results are also summarized in FIG. 2 as a plot of nanowire diameter as a function of the amount of AgNO₃ used in the nanowire synthesis and amount of DADMAN in the copolymer used in the nanowire synthesis. The product nanostructures were classified as “thin nanowires” (nanostructures less than or equal to150 nm in diameter and greater than 5 μm in length), “thick nanowires” (nanostructures greater than 150 nm in diameter and greater than 5 μm in length) and/or “nanoparticles” (nanostructures less than or equal to 5 μm in length). The plot allows the visualization of three regions, that is, a “Nanoparticles” region, wherein the silver nanostructure product was predominately nanoparticles and two nanowire regions, “Nanowires—Zone I”, wherein the silver nanostructure product was predominately thin nanowires, and “Nanowires—Zone II”, wherein the silver nanostructure product was a mixture of thin nanowires and thick nanowires, with a boundary line “C_(thin)” between the Nanoparticles region and Nanowires Zone I, and a boundary line “C_(thick)” between Nanowires—Zone I and Nanowires—Zone II.

The results plotted FIG. 2 indicate that using poly(VP-co-DADMAN) copolymer instead of poly(VP) homopolymer shifts production of thin silver nanowires toward higher concentration of silver nitrate and that synthesis of thin silver nanowires can be achieved at concentrations up to 3 times higher than in pure poly(VP) homopolymer and that this effect increases dramatically as DADMAN content of the poly(VP-co-DADMAN) copolymer increases from 0 to about 2 wt % and continues to increase, although less dramatically as the DADMAN content further increased from 2 wt % to 8%. Increasing DADMAN content above 8 wt % did not appear to provide any further significant benefit, in that poly(VP/DADMAN) copolymer having a DADMAN content of 8 wt % and poly(VP/DADMAN) copolymer having a DADMAN content of 16% each appeared to give the substantially same results.

The diameter of the silver nanowires can be determined by transmission electron microscopy (TEM) and/or scanning electron microscopy (SEM). A TEM image of the silver nanowire of Example 2A is shown in FIG. 6. The diameter of the silver nanowires of Example 2A is 55 nm.

EXAMPLE 3

The silver nanostructures of Examples 3A-3C were made substantially in accord with the process used to make the nanowires of Examples 2A-2G, as described above, using 0.5 g of the poly(VP-co-DADMAN) copolymer of Example 1E (16 wt % DADMAN content), except that the amount of silver nitrate added to the reaction mixture was varied. The length distribution of the as produced nanostructures was determined using the image analysis software “ImageJ” on picture taken with an optical microscope.

FIG. 3 shows the size distributions of the nanostructure products of Examples 3A-3C. The amount of AgNO3 used in each synthesis, as well as the symbol used to represent the nanostructure product in FIG. 3, is listed in TABLE III below.

TABLE III Symbol In AgNO₃ AgNO_(3,) Example # FIG. 3 (wt %) amount (g) 3A square 1.25 0.5 3B X 2.5 1 3C triangle 3.75 1.5

For AgNO₃ concentrations of 1.25 wt % and 2.5w %, only thin nanowires were produced, wherein the nanowires produced at 2.5 wt % AgNO₃ were significantly longer (mean length of about 20 μm) than those produced at 1.25 wt % AgNO₃ (mean length of about 10 μm. At a AgNO₃ concentration of 3.75 wt %, a mixture of thin nanowires and thick nanowires was produced.

EXAMPLE 4

The silver nanowires of Examples 4A and 4B were made according the process described above in Examples 2A-2G, using poly(VP-co-DADMAN) having al wt % DAMAN content at two different amounts of AgNO₃.

FIG. 4 shows the size distributions of the nanostructure products Examples 4A and 4B. The amount of AgNO₃ used in each synthesis, as well as the symbol used to represent the nanostructure product in FIG. 4, is listed in TABLE IV below.

TABLE IV Symbol in Zone of AgNO₃ AgNO₃ Example # FIG. 4 FIG. 2 (wt %) amount (g) 4A triangle I 1.25 0.5 4B X II 2.5 1

EXAMPLE 5

Reduced-water synthesis of poly(VP-co-DADMAN) having a 1 wt % DADMAN content

The synthesis of poly(VP-co-DADMAN) is composed of two steps:

The first step was a counter-ion exchange to form DADMAN (Diallydimethylammonium nitrate) from commercially-available DADMAC (Diallydimethylammonium chloride). To exchange the counter-ion, a solution of 13.54 g of AgNO₃ dissolved in 6.44 g of deionized water was added to 21.00 g of DADMAC in water (65 wt %). The molar ratio of AgNO₃ to DADMAC is 1 to 1.05 in order to remove all of the AgNO₃ (which would otherwise give a black color to the solution). After vortex stirring, two phases appeared. The liquid supernatant, which contained DADMAN in water, is collected. The white silver solid precipitate of AgCl is washed with 5 mL of water and then centrifuged a second time to extract all the DADMAN monomer from it. The combined supernatants were filtered through a 0.20 μm filter and added to 1452 g of vinylpyrrolidone (VP) and 130 g of molecular sieves. The monomers were shaken for an hour after which the sieves were removed. The solution was subsequently introduced into a 5-L three-necked round-bottomed flask reactor.

Initiator solution was prepared separately by adding 2.20 g of AlBN to 20.8 g (about 20 mL) of VP.

The mixture of monomers was heated up to 60° C. and stirred. 6.66 g of thiocarbonylthio transfer agent and 2.5 g of initiator solution were added to the 5-L flask. Then, 2.5 g of the initiator solution was added every 30 minutes. The reaction temperature was maintained between 57 and 62° C. After 7.5 hours, 500 g of methanol was added to the flask to reduce the viscosity of the reactant and the reaction was allowed to stir for up to 12 hours. A yellow viscous transparent liquid was obtained.

Since VP and DADMAN are soluble in diethyl ether and poly(VP-co-DADMAN) is not, the copolymer was isolated from remaining monomer by selective precipitation in this solvent. Two volumes of ether were used for 1 volume of copolymer. The ether was removed from the resulting white precipitate, which was subsequently dried in a hood and then in a vacuum oven. The dried copolymer was ground to obtain a white, slightly yellow, fine powder.

EXAMPLE 6

Alternative reduced-water synthesis of poly(VP-co-DADMAN) having a 1 wt % DADMAN content

The synthesis of poly(VP-co-DADMAN) is composed of two steps:

The first step was a counter-ion exchange to form DADMAN (Diallydimethylammonium nitrate) from commercially-available DADMAC (Diallydimethylammonium chloride). To exchange the counter-ion, a solution of 13.54 g of AgNO₃ dissolved in 6.44 g of deionized water was added to 21.00 g of DADMAC in water (65 wt %). The molar ratio of AgNO₃ to DADMAC is 1 to 1.05 in order to remove all of the AgNO₃ (which would otherwise give a black color to the solution). After vortex stirring, two phases appeared. The liquid supernatant, which contained DADMAN in water, is collected. The white silver solid precipitate of AgCl is washed with 5 mL of water and then centrifuged a second time to extract all the DADMAN monomer from it. The combined supernatants were filtered through a 0.20 μm filter and added to 1452 g of vinylpyrrolidone (VP) and 130 g of molecular sieves. The monomers were shaken for an hour after which the sieves were removed. The solution was subsequently introduced into a 5-L three-necked round-bottomed flask reactor.

Initiator solution was prepared separately by adding 2.20 g of AlBN to 20.8 g (about 20 mL) of VP.

The mixture of monomers was heated up to 60 ° C. and stirred. 6.66 g of thiocarbonylthio transfer agent and 2.5 g of initiator solution were added to the 5-L flask. Then, 2.5 g of the initiator solution was added every 30 minutes. The reaction temperature was maintained between 57 and 62° C.

After 7.5 hours, 500 g of ethylene glycol was added to the flask to reduce the viscosity of the reactant. The temperature was raised to 70° C., and another 500 g of ethylene glycol was added after one hour. The reaction was allowed stir for up to 12 hours. A yellow viscous transparent liquid was obtained.

The copolymer suspension is used as is in silver nanowire synthesis without further purification.

EXAMPLE 7

High aspect ratio silver nanowires were achieved using poly(VP-co-DADMAN) in ethylene glycol that required the addition of a base.

The pH of the ethylene glycol used (high-purity anhydrous ethylene glycol; Sigma-Aldrich Lot SHBC6651V, “Lot B”) in the reaction mixture was determined to be 4.6 by dilution and titration. The pH of the pure ethylene glycol can be read on the vertical axis, for V=0 mL, of the titration curve shown in FIG. 7. Lot B ethylene glycol was used in the present Example 7 and in the following Examples 8 and 9.

1.8 mg of lithium chloride (LiCl), 2.4 mg lithium hydroxide (LiOH), and 0.5 g poly(VP-co-DADMAN) having a 1 wt % DAMAN content were added to 44 g of ethylene glycol and heated to 175° C. for 30 minutes under nitrogen atmosphere and moderate agitation (100-300 rpm). In the seeding step, an initial amount of silver nitrate (14 mg AgNO₃ dissolved in 0.45 mL ethylene glycol) was then added into the reaction mixture. A silver nitrate feed solution (with 0.37 gm of AgNO₃ dissolved in 12 g ethylene glycol) was then fed dropwise to the reaction mixture at a rate of 1.5 mL/minute. The reaction was stopped after 15 minutes from the start of the feed by quenching the solution in ice.

The nanowires of Example 7 were isolated form the reaction mixture by gravity separation and the poly(VP-co-DADMAN residues were removed substantially according to the isolation steps described in the previous Examples.

An SEM image of the nanowires of Example 7 is shown in FIG. 8. The average diameter of the nanowires was found to be about 47 nm, and the average length was found to be about 20 μm. FIG. 9 shows an image of the nanowires of Example 7 as seen through optical microscopy.

EXAMPLE 8

The silver nanowires of Example 8 were made by an analogous process to that used to make the silver nanowires of Example 7, except that LiOH was replaced with 5.8 mg of potassium hydroxide (KOH).

FIG. 10 shows an image of the nanowires of Example 8 as seen through optical microscopy. The average diameter of the nanowires of Example 8 was found to be about 65 nm, and the average length was found to be about 25 μm.

EXAMPLE 9

The silver nanowires of Example 9 were made by an analogous process to that used to make the silver nanowires of Example 7, except that LiOH was replaced with 4.1 mg of sodium hydroxide (NaOH).

FIG. 11 shows an image of the nanowires of Example 9 as seen through optical microscopy. The average diameter of the nanowires of Example 9 was found to be about 57 nm, and the average length was found to be about 22 μm. 

What is claimed is:
 1. A process for making silver nanostructures, comprising reacting at least one polyol and at least one silver compound that is capable of producing silver metal when reduced, in the presence of: (a) a source of chloride or bromide ions, and (b) at least one copolymer that comprises: (i) one or more first constitutional repeating units that each independently comprise at least one pendant saturated or unsaturated, five-, six-, or seven-membered, acylamino- or diacylamino-containing heterocylic ring moiety per first constitutional repeating unit, and (ii) one or more second constitutional repeating units, each of which independently differs from the one or more first constitutional repeating units, and has a molecular weight of greater than or equal to about 500 grams per mole.
 2. The process of claim 1, wherein the first constitutional repeating units of the copolymer each independently comprise a pyrrolidonyl moiety or a pyrrolidinedionyl moiety and the second constitutional repeating units of the copolymer each independently comprise a cationic moiety.
 3. The process of claim 2, wherein, wherein the copolymer is a random copolymer made by free radical polymerization of vinyl pyrrolidone, vinyl caprolactam, or vinyl pyrrolidone and vinyl caprolactam with one or more ethylenically unsaturated cationic monomers.
 4. The process of claim 3, wherein the one or more ethylenically unsaturated cationic monomers are selected from dimethylaminomethyl (meth)acrylate, dimethylaminopropyl (meth)acrylate, di(t-butyl)aminoethyl (meth)acrylate, dimethylaminomethyl (meth)acrylamide, dimethylaminoethyl (meth)acrylamide, dimethylaminopropyl (meth)acrylamide, vinylamine, vinyl imidazole, vinylpyridine, vinylpyrrolidine, vinylpyrroline, vinylpyrazolidine, vinylpyrazoline, vinylpiperidine, vinylpiperazine, vinylpyridine, vinylpyrazine, vinylpyrimadine, vinylpyridazine, trimethylammonium ethyl (meth)acrylate salts, dimethylammonium ethyl (meth)acrylate salts, dimethylbenzylammonium (meth)acrylate salts, benzoylbenzyl dimethylammonium ethyl(meth) acrylate salts, trimethyl ammonium ethyl (meth)acrylamido salts, trimethyl ammonium propyl (meth)acrylamido salts, vinylbenzyl trimethyl ammonium salts, and diallyldimethyl ammonium salts.
 5. The process of claim 4, wherein the copolymer is a random copolymer made by free radical polymerization of a monomer mixture comprising from about 80 to less than 100 parts by weight of vinyl pyrrolidone and from greater than 0 to about 20 parts by weigh of a diallyldimethylammonium salt.
 6. The process of claim 1, wherein the at least one silver compound comprises silver nitrate, the at least one polyol comprises ethylene glycol, the total amount of silver nitrate added to the reaction mixture is from 1.5×10⁻² mole to about 1 mole silver nitrate per Liter of reaction mixture, and the reaction is conducted in the presence of, based on the weight of the reaction mixture, from about 0.1 wt % to about 20 wt % of the copolymer.
 7. The process of claim 1, wherein the at least one polyol has a pH of from about 1 to about
 14. 8. The process of claim 1, wherein the at least one polyol has a pH of from about 5 to about
 12. 9. The process of claim 1, wherein the at least one polyol has a pH of from about 7 to about
 10. 10. A process for making silver nanostructures, comprising reacting at least one polyol and at least one silver compound that is capable of producing silver metal when reduced, in the presence of: (a) a source of chloride or bromide ions, and (b) at least one copolymer that comprises: (i) one or more first constitutional repeating units that each independently comprise at least one pendant saturated or unsaturated, five-, six-, or seven-membered, acylamino- or diacylamino-containing heterocylic ring moiety per first constitutional repeating unit, and (ii) one or more second constitutional repeating units, each of which independently differs from the one or more first constitutional repeating units, and has a molecular weight of greater than or equal to about 500 grams per mole; and (c) at least one base.
 11. The process of claim 10, wherein the at least one base comprises sodium hydroxide, lithium hydroxide, potassium hydroxide, or mixtures thereof. 